Slope Reliability Analysis Considering  Corrosion-induced Degradation of Cables’ Performance

JIANG Shui-hua; WEI Bo-wen; LI Cong

doi:10.11988/ckyyb.20151043

PDF(1761 KB)

Journal of Changjiang River Scientific Research Institute ›› 2017, Vol. 34 ›› Issue (3) : 90-95. DOI: 10.11988/ckyyb.20151043

ROCK-SOIL ENGINEERING

Slope Reliability Analysis Considering Corrosion-induced Degradation of Cables’ Performance

JIANG Shui-hua¹,WEI Bo-wen¹,LI Cong²

Author information +

History +

Abstract

Degradation of pre-stressed cable’s performance caused by corrosion has significant effect on slope stability. In this research, two typical failure modes of pre-stressed cables in the presence of corrosion are identified, and the corresponding time-dependent anchored force models are established. The representative section Ⅱ₁-Ⅱ₁of abutment slope at the left bank of Jinping I-stage Hydropower Station is taken as an example to illustrate the time-dependent slope stability and reliability of the slope excavated to elevation 1780 m and reinforced with three shear-resistant concrete plugs and pre-stressed cables under three conditions. Results indicate that the corrosion of pre-stressed cables has significant effect on both the stability and reliability of anchored slope. In the early stage (the first 120 years) of cable’s service life, the variations in the factor of safety and probability of slope failure are relatively small; whereas in the later stage, the variations increased sharply and the stability condition deteriorates rapidly. Hence, reasonable periodical maintenance is required for the in-service anchored structures such as pre-stressed cables subject to corrosive underground environments. In addition, the influences of variabilities and cross-correlations of shear strength parameters of rock masses and structural planes on the slope stability can be effectively accounted for in the slope reliability analysis.

Key words

pre-stressed cable / cable corrosion / Jinping I-stage Hydropower Station / anchored slope / reliability

Cite this article

EndNote

Ris (Procite)

Bibtex

Download Citations

JIANG Shui-hua,WEI Bo-wen,LI Cong. Slope Reliability Analysis Considering Corrosion-induced Degradation of Cables’ Performance[J]. Journal of Changjiang River Scientific Research Institute. 2017, 34(3): 90-95 https://doi.org/10.11988/ckyyb.20151043

References

[1] 丁多文, 白世伟, 罗国煜. 预应力锚索加固岩体的应力损失分析[J]. 工程地质学报, 1995, 3(1): 65-69.
[2] XANTHAKOS P P. Ground Anchors and Anchored Structures[M]. New York: John Wiley and Sons, 1991.
[3] 高大水, 吴海斌, 王莉. 三峡船闸高边坡预应力锚索耐久性研究[J]. 岩土力学, 2005, 26(增2): 126-130.
[4] 郑静, 曾辉辉, 朱本珍. 腐蚀对锚索力学性能影响的试验研究[J]. 岩石力学与工程学报, 2010, 29(12): 2469-2474.
[5] 曾辉辉, 朱本珍, 高志华. 强腐蚀环境下锚索强度指标及表观特性试验研究[J]. 水利与建筑工程学报, 2011, 9(2): 48-53.
[6] LI F, LIU Z, ZHAO Y, et al. Experimental Study on Corrosion Progress of Interior Bond Section of Anchor Cables under Chloride Attack[J]. Construction and Building Materials, 2014, 71: 344-353.
[7] 许明, 唐树名, 李强, 等. 单锚及群锚失效对边坡稳定性影响的模型试验研究[J]. 岩石力学与工程学报, 2007, 26(增1): 2755-2760.
[8] 李英勇, 张顶立, 张宏博, 等. 边坡加固中预应力锚索失效机制与失效效应研究[J]. 岩土力学, 2010, 31(1): 144-150.
[9] 郑筱彦, 夏元友. 群锚对岩质边坡稳定性影响的数值模拟研究[J]. 武汉理工大学学报: 交通科学与工程版, 2011, 35(2): 275-279.
[10]ZHENG W, ZHUANG X, CAI Y. On the Seismic Stability Analysis of Reinforced Rock Slope and Optimization of Prestressed cables[J]. Frontiers of Structural and Civil Engineering, 2012, 6(2): 132-146.
[11]牛荻涛. 混凝土结构耐久性与寿命预测 [M]. 北京: 科学出版社, 2003.
[12]洪海春, 徐卫亚. 全长粘结式预应力锚索锈胀开裂时服务年限研究[J]. 岩土力学, 2008, 29(4): 949-953.
[13]曾宪明, 雷志梁, 张文巾,等. 关于锚杆“定时炸弹”问题的讨论——答郭映忠教授[J]. 岩石力学与工程学报, 2002, 21(1): 143-147.
[14]范宇洁, 郑七振, 魏林. 预应力锚索锚固体的破坏机理和极限承载能力研究[J]. 岩石力学与工程学报, 2005, 24(15): 2765-2769.
[15]惠云玲, 林志伸. 锈蚀钢筋性能试验研究分析[J]. 工业建筑, 1997, 27(6): 10-13.
[16]DU Y G, CLARK L A, CHANA H C. Residual Capacity of Corroded Reinforcing Bars[J]. Magazine of Concrete Research, 2005, 57(3): 135-147.
[17]LI L, LIANG R Y, LIU H. System Reliability Analysis for Anchor-stabilised Slopes Considering Stochastic Corrosion of Anchors[J]. Structure and Infrastructure Engineering, 2015, 11(10): 1294-1305.
[18]BHARGAVA K,GHOSH A K,MORI Y,et al.Corrosion-induced Bond Strength Degradation in Reinforced Concrete: Analytical and Empirical Models[J]. Nuclear Engineering and Design, 2007, 237(11): 1140-1157.
[19]国家电力公司成都勘测设计研究院. 雅砻江锦屏一级水电站可行性研究报告(3): 工程地质[R]. 成都: 国家电力公司成都勘测设计研究院,2003.
[20]漆祖芳,姜清辉,唐志丹,等. 锦屏一级水电站左岸坝肩边坡施工期稳定分析[J]. 岩土力学,2012, 33(2): 531-538.
[21]蒋水华, 李典庆, 黎学优, 等. 锦屏一级水电站左岸坝肩边坡施工期高效三维可靠度分析[J]. 岩石力学与工程学报, 2015, 34(2): 349-361.
[22]王继敏, 段绍辉, 胡书红. 锦屏一级水电站左岸坝肩复杂地质条件高陡边坡处理[J]. 岩石力学与工程学报, 2012, 31(8): 1597-1605.
[23]TANG X S, LI D Q, CHEN Y F, et al. Improved Knowledge-based Clustered Partitioning Approach and Its Application to Slope Reliability Analysis[J]. Computers and Geotechnics, 2012, 45: 34-43.
[24]蒋水华, 李典庆, 周创兵. 基于拉丁超立方抽样的边坡可靠度分析非侵入式随机有限元法[J]. 岩土工程学报, 2013, 35(增2): 70-76.
[25]李宁, 张鹏, 于冲. 边坡预应力锚索加固的数值模拟方法研究[J]. 岩石力学与工程学报, 2007, 26(2): 254-261.
[26]洪海春. 边坡岩体锚固性能研究及其工程应用[D]. 南京:河海大学, 2007.
[27]赵树光. 岩质边坡预应力锚杆(索)应力分布规律及工程应用研究[D]. 南京:河海大学, 2007.
[28]HOEK E. Practical Rock Engineering[M]. https:∥www.rocscience.com/documents/hoek/corner/Practical-Rock-Engineering-Full-Text.pdf, 2007.
[29]BISHOP A W.The Use of Slip Circle in the Stability Analysis of Slopes[J].Géotechnique,1955,5(1):7-17.