复合水泥土无侧限抗压强度正交试验研究

王贤昆,庞建勇,王强

作者信息 +

Orthogonal Experimental Studies on Unconfined Compressive Strength ofComposite Cement-soil

WANG Xian-kun,PANG Jian-yong,WANG Qiang

Author information +

文章历史 +

摘要

脱硫石膏与粉煤灰混合后可复合成一种新型活性胶凝材料,针对其在工程中的运用情况,采用正交试验法研究了不同养护龄期下水泥掺量、脱硫石膏及粉煤灰对水泥土抗压强度的影响,分析了各因素水平之间的差异。研究结果表明:水泥掺量对水泥土无侧限抗压强度影响最大,脱硫石膏与粉煤灰在3 d时对水泥土的无侧限抗压强度基本无影响,后期随着龄期的增大对其有一定影响;同时脱硫石膏在28 d前对水泥土的无侧限抗压强度影响比粉煤灰稍显著,28 d后粉煤灰的影响则稍显著。

Abstract

Flue-gas desulfurization gypsum and fly ash can be blended into a new cementitious material with chemical activity.According to its application in the engineering,contents of flue-gas desulfurization gypsum,fly ash and cement were taken as variable parameters in the experiment.The effects of the three factors on compressive strength of cement-soil with different curing ages were explored through orthogonal experiment.Meanwhile,differences among these factors were analyzed.The results show that,cement blending ratio has the maximum impact on the unconfined compressive strength of cement-soil,whereas flue-gas desulfurization gypsum and fly ash have almost no effect on the unconfined compressive strength of cement-soil in the age of 3 days,and a little impact at late stage.Moreover,the influence of flue-gas desulfurization gypsum is more significant than that of fly ash within 28 days,but after that,the impact of fly ash is more significant than that of flue-gas desulfurization gypsum.

导出引用

王贤昆,庞建勇,王强. 复合水泥土无侧限抗压强度正交试验研究[J]. 长江科学院院报. 2015, 32(12): 72-75 https://doi.org/10.11988/ckyyb.20140537

WANG Xian-kun,PANG Jian-yong,WANG Qiang. Orthogonal Experimental Studies on Unconfined Compressive Strength ofComposite Cement-soil[J]. Journal of Changjiang River Scientific Research Institute. 2015, 32(12): 72-75 https://doi.org/10.11988/ckyyb.20140537

中图分类号： TU411.6

参考文献

[1] 胡健民.脱硫石膏的综合利用[J].上海电力,2006,(5):480-483.(HU Jian-min.Comprehensive Utilization of the Desulphurization Gypsum[J].Shanghai Electric Power,2006,(5):480-483.(in Chinese))
[2] 王方群,原永涛,齐立强.脱硫石膏性能及其综合利用[J].粉煤灰综合利用,2004,(1):41-44.(WANG Fang-qun,YUAN Yong-tao,QI Li-qiang.Properties and Comprehensive Utilization of the Desulphurization Gypsum[J].Fly Ash Comprehensive Utilization,2004,(1):41-44.(in Chinese))
[3] 李云雁,胡传荣.试验设计与数据处理[M].北京:化学工业出版社,2005:41-52.(LI Yun-yan,HU Chuan-rong.Experimental Design and Data Processing[M].Beijing:Chemical Industry Press,2005:41-52.(in Chinese))
[4] 黄丽娟.粉煤灰对水泥土抗压强度影响的正交试验研究[J].河南理工大学学报(自然科学版),2009,28(3):352-356.(HUANG Li-juan.Orthogonal Experimental Studies on the Influence of Fly Ash to the Compressive Strength of Cement-soil[J].Journal of Henan Polytechnic University(Natural Science),2009,28(3):352-356.(in Chinese))
[5] 陈瑜,高英力,王盛铭.粉煤灰-脱硫石膏双掺砂浆试验研究与应用[J].长沙理工大学学报:自然科学版,2010,7(2):48-52.(CHEN Yu,GAO Ying-li,WANG Sheng-ming.Experimental Study and Application of Fly Ash-desulfurization Gypsum Double Blended Mortar[J].Journal of Changsha University of Science and Technology:Natural Science,2010,7(2):48-52.(in Chinese))
[6] 郭大江,袁运法,胡浩然,等.脱硫石膏性能研究及其在普通硅酸盐水泥中的应用[J].硅酸盐通报,2010,29(2):22-26.(GUO Da-jiang,YUAN Yun-fa,HU Hao-ran,et al.Influence of FGD Gypsum on the Properties of Portland Cement[J].Bulletin of the Chinese Ceramic Society,2010,29(2):22-26.(in Chinese))
[7] 童小东,徐敏,戴国亮,等.某添加剂在水泥土搅拌法中的应用[J].东南大学学报(自然科学版),2007,37(2):345-349.(TONG Xiao-dong,XU Min,DAI Guo-liang,et al.Application of An Additive in Cement Deep Mixing Method[J].Journal of Southeast University(Natural Science Edition),2007,37(2):345-349.(in Chinese))
[8] 袁聚云,景路,李阳,等.脱硫石膏土体增强剂用于深层搅拌桩的试验研究[J].岩土工程学报,2011,33(增1):23-28.(YUAN Ju-yun,JING Lu,LI Yang,et al.[J].Chinese Journal of Geotechnical Engineering,2011,33(Sup.1):23-28.(in Chinese))
[9] 王迪,朱梦良,陈瑜,等.脱硫石膏-粉煤灰复合胶凝材料基胶砂试验研究[J].粉煤灰综合利用,2009,(5):7-10.(WANG Di,ZHU Meng-liang,CHEN Yu,et al.Study on Composite Material Produced by Desulphurization Gypsum-fly Ash[J].Fly Ash Comprehensive Utilization,2009,(5):7-10.(in Chinese))
[10]高英力,陈瑜,王迪,等.脱硫石膏-粉煤灰活性掺合料设计及水化特性[J].四川大学学报:工程科学版,2010,42(2):225-231.(GAO Ying-li,CHEN Yu,WANG Di,et al.Design and Hydration Characteristics of Desulphurization Gypsum-fly Ash Active Admixture[J].Journal of Sichuan University:Engineering Science,2010,42(2):225-231.(in Chinese))
[11]郭晓潞,施惠生.脱硫石膏粉煤灰地聚合物抗压强度和反应机理[J].同济大学学报(自然科学版),2012,40(4):573-577.(GUO Xiao-lu,SHI Hui-sheng.Compressive Strength and Mechanism of Geopolymers from Flueas Gypsum and Fly Ash[J].Journal of Tongji University (Natural Science),2012,40(4):573-577.(in Chinese))
[12]高英力,陈瑜,马保国.粉煤灰-脱硫石膏水泥基材料水化活性及微结构[J].土木建筑与环境工程,2011,33(5):137-142.(GAO Ying-li,CHEN Yu,MA Bao-guo.Microstructure and Hydration Activity of Cement-based Materials Containing Fly Ash Desulphurization Gypsum[J].Journal of Civil, Architectural & Environmental Engineering,2011,33(5):137-142.(in Chinese ))
[13]陈瑜,高英力.粉煤灰脱硫石膏复合胶凝材料的配合比与水化[J].建筑材料学报,2012,15(2):283-288.(CHEN Yu,GAO Ying-li.[J].Journal of Building Materials,2012,15(2):283-288.(in Chinese))